Fa'ata'ita'iga o Fa'asinoga Fa'asinoga a le PVC Flame Retardant Masterbatch
Fuafuaga ma le fa'ata'ita'iina o le fa'aogaina o le fa'alumaina o le afi o le PVC, fa'atasi ai ma fa'agata mumu o lo'o i ai ma vaega autu fa'atasi, fa'atatau i le UL94 V0 fa'aletonu afi (fa'afetaui i le V2 e ala i le fa'aitiitia o aofa'iga fa'aopoopo).
I. Fautuaga Fuafua Fa'avae (PVC Malosi)
Fa'apalapala Fa'asa'o Mumu:
| Vaega | utaina (wt%) | Fa'amatalaga Galuega |
|---|---|---|
| PVC resini (ituaiga SG-5) | 40-50% | Mea matrix, sili ona maualalo le suau'u suau'u togi |
| Alumini hypophosphite | 12-15% | Punavai oona mo le fa'atupuina o malala, e taofiofia le susulu |
| Zinc borate | 8-10% | Fa'atasi le asu o le asu, tali atu i le HCl mai le fa'aleagaina o le PVC |
| Aluminium hydroxide ua suia i luga | 10-12% | Endothermic malulu, e mana'omia le silane so'o fa'apipi'i fa'apipi'i fa'apipi'i (tetee fa'aleagaina. e fetaui ma le faiga o le PVC) |
| Antimony trioxide (Sb₂O₃) | 3-5% | Core synergist, faʻaleleia le mumu o le afi e ala ile Cl-Sb synergy |
| Zinc molybdate (tetee asu) | 5-8% | Fa'aopoopo fa'aopoopo, fa'aitiitia le mamafa o le asu (ki mo le tausisia o le DIN 4102) |
| Dipentaerythritol (DPE) | 2-3% | Fesoasoani fa'asolo, fa'aleleia le pulea o le liusuavai |
| Fa'amautu fa'avevela (Ca-Zn composite) | 3-4% | E taua e puipuia ai le faʻaleagaina o le vevela i le taimi o le gaosiga |
| Plasticizer (DOP po'o le eco-alternative) | 0-8% | Fetuuna'i mo le maaa (filifili mo PVC malo) |
| Lubricant (calcium stearate) | 1-1.5% | Fa'aleleia le fa'agaioiina, puipuia le pipii o le uila |
| Fesoasoani ile fa'agaioiina (ACR) | 1-2% | Faʻaleleia le faʻapipiʻiina ma le faʻasalalau masterbatch |
II. Fa'avae Autū Fa'atonu
- Faiga Fa'amumū Mumu
- Cl-Sb Synergy: O le chlorine (56%) o le PVC fa'atasi ma le 3-5% Sb₂O₃ e fausia ai se pa puipui o le SbCl₃, e mafai ai ona fa'aletonu le mumu o le kesi/condensed-phase.
- Taofi le asu: Zinc molybdate + zinc borate e faʻaitiitia ai le mamafa o le asu e> 40% (ASTM E662).
- Fa'aleleia o le Sia: Alumini hypophosphite + DPE e fa'atupuina le feso'ota'iga feso'ota'iga phosphoric ester char i le 200–250°C, e fa'amalieina ai le le lava o le char i le amataga o le PVC.
- Gaioiina Fetuuna'i
- Faʻatusatusaga o le vevela: Alumini hypophosphite (decomposition ≥250 ° C) ma luga-faʻaleleia Al (OH) ₃ (mautu i> 200 ° C) suʻega PVC gaioiga (160-190 ° C).
- Faʻamautinoaga mautu: Ca-Zn stabilizers puipuia le faʻaleagaina o resini mai le faʻamalolo HCl; E fesoasoani le ACR i le faʻapipiʻiina i faiga faʻatumu maualuga.
- Paleni o Galuega
- Aofa'i afi mumu uta uta: 35-45%, tensile malosi taofi ≥80% (masani ≥40 MPa mo PVC malo).
- Mo le fetu'una'i (PVC fe'avea'i), sui le DOP ile 8% suau'u soya epoxidized (lua palasitika/mu mumu).
III. Su'ega & Fa'amaoniga Fua
Fa'aletonu le afi:
- UL94 V0 (1.6 mm mafiafia)
- Fa'atapula'aina o le Fa'asinoala o Okesene (LOI) ≥32%
Pulea asu:
- Su'ega ole potu asu ole NBS: Tulaga maualuga fa'apitoa fa'apitoaDs≤150 (faiga mu)
Meatotino Fa'ainisinia:
- Malosiaga tensile ≥35 MPa (malosi), elongation i le malologa ≥200% (fetuunai)
Fa'amaumau vevela:
- E fa'amaonia e le DMA e leai se pa'u fa'aopoopo ile 180°C.
IV. Tau & Fetuunaiga Fa'alelei
Su'i Tau maualalo:
- Fa'aititia le zinc molybdate ile 3%, sui vaega ole Al(OH)₃ ile Mg(OH)₂ (fa'ateleina ile 15%).
Fofo e leai se Antimony:
- Aveese le Sb₂O₃, faʻaaoga le 2% alumini diethylphosphinate + 5% nano-kaolin (laʻititi laʻititi le lelei; manaʻomia le 3 mm mafiafia mo V0).
Asu Fa'amuamua:
- Faaopopo le 1% silicone resin-coated carbon black e faʻaititia atili ai le asu i le 15%.
V. Fa'asologa o Ta'iala
- Fa'asologa Fa'afefiloi:
PVC resin → stabilizer + lubricant → mumu mumu (maualalo i le maualuga density) → plasticizer (fasi-faaopoopo mulimuli). - Fa'agasologa o le vevela:
Sone extruder twin-screw: 160°C (fafaga) → 170°C (liusuavai) → 180°C (faafefiloi) → 175°C (ulu oti). - Masterbatch Concentration:
Fautuaina 50% uta; fa'asusu le 1:1 ma le PVC taupou mo le fa'aaogaina o tui tui.
O lenei fua fa'atatau e faapaleni ai le mu maualuga, maualalo le asu, ma le mautu o gaioiga. O fa'ata'ita'iga la'ititi e fautuaina a'o le'i fa'afua, fa'atasi ai ma fetuutuuna'iga e fa'atatau i fomu oloa (pepa, uaea, ma isi).